N04400合金冷軋板耐腐蝕性能
發布日期：2022-11-22 瀏覽次數：770
合金400是一種單相固溶鎳銅合金，從零到800°F在溫度范圍內，它對許多腐蝕性環境具有良好的抵抗力。這種合金只能通過冷處理而不是熱處理來硬化。這種合金的居里溫度在環境溫度范圍內，受到合金化學成分變化的影響。建議在需要強非磁性特性的應用中要小心。400合金中的銅鎳比幾乎與金屬礦中的銅鎳比相同。
| UNS No. | N04400 – BSI No. BS3074NA13 |
| Chemical Comp. (%) | Ni 63 min / Cu 28 ~ 34 / Fe 2.5 max / Mn 2.0 max / C 0.3 max / Si 0.5 max / S 0.024 max |
| ASTM Spec. | B163, B165, B828 |
| ASME Spec. | SB163, SB165, SB828 |
| Applications | Marine engineering, chemical and hydro-carbon processings, heat exchangers and alkylation units. |
| Temper | Annealed / Stress Relieved |
| Properties * | Metric | English |
| Density | 8.80 g/cc | 0.318 lb/in3 |
| Tensile Strength – Annealed min. | 483 MPa | 70 ksi |
| Tensile Strength – Stress Relieved min. | 586 MPa | 85 ksi |
| Yield Strength – Annealed min. | 193 MPa | 28 ksi |
| Yield Strength – Stress Relieved min. | 379 MPa | 55 ksi |
| CTE, linear | 14.2 μm/m•°C @ 100°C | 7.7 in/in/°F x 10-6 @ 200°F |
| Specific Heat Capacity | 445 J/kg•°C @ 100oC | 0.105 Btu/lb/°F @ 200oF |
| Thermal Conductivity | 24.0 W/m•°C @ 100°C | 167 Btu-in/h/ft2/°F @ 200°F |
| Melting Point | 1300 – 1350 °C | 2370 – 2460 °F |
耐腐蝕性
400合金具有耐多種還原介質腐蝕的特性。它是為數不多的可接觸氟、氫氟酸、氟化氫或其衍生物的合金之一。特殊的抗性已被證明在所有濃度達到沸點的氫氟酸中。400合金還可以抵抗各種形式的硫酸和鹽酸。良好的耐海水腐蝕性。
制造和熱處理
典型的成型、成型、機加工和連接操作可用于制造400合金。熱加工作業應在1200點°F至2150°F兩者之間進行。對于嚴重還原，應使用1700°F和2150°F兩者之間的溫度。冷加工應在退火材料上進行。根據所需的機械性能，合金400可用的熱處理包括應力平衡、應力消除和退火。應力平衡在575°F在溫度下進行3小時，然后快速淬火。這樣可以在不影響其他性能的情況下增加屈服強度。應力消除在1000°F到1050°F在1到2小時的溫度下，然后慢慢冷卻。這將降低應力而不產生再結晶晶粒結構，建議在金屬去除后減少變形。退火將軟化加工硬化材料，并在1600°F和1800°F保持2到10分鐘，然后快速淬火。
工業與應用
400合金廣泛應用于各種行業，特別是在海洋工業和化工行業。典型的應用包括泵和閥門、傳動軸、船舶固定裝置和緊固件、電子部件、彈簧、化學處理設備、淡水和鹽水罐、工藝容器和管道、鍋爐供水加熱器和其他熱交換器。